not much different....you wont have the slag that rod leaves...the application is mostly the same....you hold the nozzle at about the 45* like rod welding....I like either push or pull method...it takes a touch of practice but if you've had enough experience then you will fall into it very easily...I love it for filling large gaps or cracks...dont have to slag at all...just keep applying filler wire til it is filled. Overhead will take you a little time to get your hand and eye and settings....but, works like a charm........good luck
[