NiCrBSi

4.9

Price: $42.00 / Kg
  • Min. Order:5 KG
  • Product Code:8113001090
  • Model:NiCrBSi(150-53um/100-270mesh)
  • Processing Level:NiCrBSi
  • Grade:NiCrBSi
  • Finished goods inventory:550 KG
  • N.W:500 KG
  • Specification:150-53um/100-270 Mesh
  • Tolerance:150-53um/100-270 Mesh
  • Delivery time:In stock, shipment at any time
  • Origin:China chengdou
  • Shipping:Free Shipping to United States via ePacket
Payment:
  • Operator telephone:0086 13808223868
  • Operator email:sales-manager201@wococarbide.com

Product Image

Details Image

Design Image

Composition

Fe (%):2.37 B (%)1.84 Si (%)3.14 Ni Balanc. Cr (%)0.45 O(%)0.05.

Performance Index

+150um 3.4% -150/+100um 53.7% -100+53um 38.2% -53um 4.7%

Packing Instructions

carton and iron drum

Description

Ultra-high-speed laser cladding technology is mainly used to improve the wear resistance, corrosion resistance, high temperature resistance, and oxidation resistance of the surface of the parts, so as to achieve the goal of surface modification or repair, and meet the requirements for the specific performance of the material surface. In the conventional laser cladding process, the laser energy is mainly used to melt the base material to form a molten pool. The powder is poured into the molten pool and melted, and then solidified to form a protective coating.



The ultra-high-speed laser cladding technology essentially changes the melting position of the powder, so that the powder will be melted by the laser at the top of the workpiece, and then uniformly coated on the surface of the workpiece. Its cladding rate can be as high as 20-200m/min. Due to the low heat input, this technology can be used for surface cladding of heat-sensitive materials, thin-walled and small-sized components, and it can be used for brand-new material combinations, such as aluminum-based materials, Preparation of coatings on titanium-based materials or cast iron materials. Because the surface quality of the coating is significantly higher than that of ordinary laser cladding, it can be applied only by simple grinding or polishing, so the waste of materials and subsequent processing are greatly reduced. Ultra-high-speed laser melting is in terms of cost, efficiency, and thermal impact on parts. Covering has irreplaceable application advantages.